Plasticizer Migration - an overview | ScienceDirect Topics
Plasticizer migration from one material to another causes problems with their performance. 1, 4 Figure 10.65 shows that plasticizer migration increases with the increase in the plasticizer concentration in PVC. The migration process follows Fickian diffusion and can be approximated from the following equation:
Plasticiser loss from plastic or rubber products through
Plasticisers are commonly added to polymers to lower their glass transition temperature and increase their processability, mechanical flexibility, ductility and toughness. 1, 2, 3, 4, 5 They...
Methods for determination of plasticizer migration
Plasticizer migration is responsible for premature coating failure in polyvinyl chloride (PVC) synthetic materials that continue to benefit our daily life as a reliable and cost-efficient simulant of genuine leather. In this context, the establishment of standard assays that measure the migration rate of plasticizers under varying scenarios plays a pivotal role in comparing durability of those
Common Signs Of Plasticizer Migration - Chaffee Industrial
When the plasticizer leaks from a PVC roof, it will cause cracks, splits, and welded sections to break apart. Combining plasticizer migration with foul weather means disaster for your roof. Early spotting of the common signs of plasticizer migration helps protect your roof. Let’s take a look at some of the telltale indicators.
Know your Plasticizers: A New Study on Plasticizer Migration
To address this phenomenon, Teknor Apex (Pawtucket, RI) has published a study focusing on plasticizer migration, which can affect a range of medical device components, including connectors. "Most PVC applications are connected to a rigid non-PVC material, and that rigid material typically is more attracted to the plasticizer than the PVC device
- What happens if a plasticizer migrates?
- Serious migration may result in substantial loss of plasticizer with resultant stiffening of the PVC. An example of plasticizer migration is softening of nitrocellulose or acrylic lacquer following prolonged contact with plasticized PVC.
- What is an example of plasticizer migration?
- An example of plasticizer migration is softening of nitrocellulose or acrylic lacquer following prolonged contact with plasticized PVC. In plasticized PVC film used for tape application, plasticizer migration to the adhesive layer can cause softening and loss of adhesion. 2017, Handbook of Plasticizers (Third Edition) GEORGE WYPYCH, ...
- Do Plasticizers improve the migration resistance of plasticized PVC material?
- This indicates that a moderate increase in the relative molecular weight of the plasticizer can effectively improve the migration resistance of the plasticized PVC material, a finding consistent with the results from the resistance tests. There has been no clear evidence observed regarding the plasticization process of plasticizers in PVC.
- How do we detect plasticizer migration from PVC synthetic materials?
- To this end, this review is compiled as a general review of the methods now available for detecting plasticizer migration from PVC synthetic materials via three different mechanisms (i.e., volatilization, exudation, and extraction), with an emphasis on the instrumentation, methodology, advantages, and limitations of each method.
- Does plasticizer migration cause premature coating failure?
- Journal of Leather Science and Engineering 4, Article number: 8 (2022) Cite this article Plasticizer migration is responsible for premature coating failure in polyvinyl chloride (PVC) synthetic materials that continue to benefit our daily life as a reliable and cost-efficient simulant of genuine leather.
- Why are new plasticizers a problem?
- The main problem in developing new plasticizers is to find a compound providing good mechanical properties to PVC, but with limited migration, extraction resistance and low volatility. There are a lot of studies describing novel plasticizers that exhibit excellent migration resistance at the expense of the deterioration of mechanical properties.